P265GH
2023-05-17 15:29:07
來源:鋼鐵之家
閱讀量:0
牌號
P265GH
歐標(biāo)鋼號
1.0425
對應(yīng)標(biāo)準(zhǔn)
EN 10222-2-2017
壓力用途用鋼制鍛件 第2部分 具有高溫特性的鐵素體和馬氏體鋼 Steel Forgings for Pressure Purposes. Part 2:Ferritic and Martensitic Steels with Specified Elevated Temperature Properties
歸類
碳鋼
P265GH 化學(xué)元素成分含量(%)
成分
C
Si
Mn
P
S
Cr
Ni
Cu
Mo
Ti
V
Nb
更多
最小值
-
-
0.5
-
-
-
-
-
-
-
-
-
Cr+Cu+Mo+Ni≤0.70
最大值
0.2
0.4
1.4
0.03
0.025
0.3
0.3
0.3
0.08
0.03
0.02
0.01
P265GH 機(jī)械性能
厚度
t
mm
熱處理或狀態(tài)
抗拉強(qiáng)度 σb
Mpa
屈服點(diǎn) σs
Mpa
斷后伸長率或延伸率 δ
%
沖擊吸收能量 KV2
J
t≤60
奧氏體化或固溶退火,890~950℃,空冷
410~530
≥245
I:≥29,tr/t:≥27
I:≥40,tr/t:≥27
60<t≤100
奧氏體化或固溶退火,890~950℃,空冷
410~530
≥215
I:≥26,tr/t:≥24
I:≥40,tr/t:≥27
① I = longitudinal to main forging directions;tr = transverse to main forging directions;t = tangential.
② Maximum room temperature for the impact test is 20 °C. By option, impact testing may be carried out at 0°C, with the condition to fulfil the impact values as stated in this table.
③ Until the yield point criteria are harmonized in the various national codes, determination of ReH may be replaced by determination of Rp0.2. In this case Rp0.2 values are 10 MPa lower for ReH values up to 355 MPa and 15 MPa lower for ReH values greater than 355 MPa.
1 近似對照表 鍋爐和壓力容器用鋼板
中國
日本
美國
國際標(biāo)準(zhǔn)組織
歐標(biāo)
俄羅斯
GB
JIS
ASTM
ISO
EN
數(shù)字牌號
GOST
Q245R
SEV245
Gr.65(450)
P265GH
P265GH
1.0425
16ГС
2 近似對照表 碳素結(jié)構(gòu)鋼和工程用鋼
日本
美國
國際標(biāo)準(zhǔn)組織
德國
法國
歐標(biāo)
俄羅斯
瑞典
英國
JIS
ASTM
ISO
W-Nr.
NF EN/NF
EN
數(shù)字牌號
GOST
SS
BS EN/BS
SG295
A414E
A516Gr.60 Gr.A
F5
F7
1.0425
A42AP
A42CP A42F
P265GH
1.0425
16K
20K
1430
1431
151-400
161-430 161Gr.400 164Gr.400 244Gr.400
注:本資料來源于互聯(lián)網(wǎng)的公開資源整理,我們不保證這些資料的準(zhǔn)確性、完整性和適用性。這些資料僅供您參考,不應(yīng)用于任何商業(yè)用途或決策依據(jù)。本資料所記載的技術(shù)信息是說明產(chǎn)品的代表性特點(diǎn)和性能的參考值,對于因誤用或不當(dāng)使用本資料所記載的信息等而造成的損害恕難承擔(dān)責(zé)任,敬請周知。