S355J2W
2023-05-15 08:48:00
來(lái)源:鋼鐵之家
閱讀量:0
牌號(hào)
S355J2W
歐標(biāo)鋼號(hào)
1.8965
對(duì)應(yīng)標(biāo)準(zhǔn)
EN 10025-5-2019
熱軋結(jié)構(gòu)鋼-第5部分:耐候結(jié)構(gòu)鋼 Hot rolled products of structural steels-Part 5: Technical delivery conditions for structural steels with improved atmospheric corrosion resistance
歸類
合金鋼
標(biāo)簽
耐候結(jié)構(gòu)鋼
鎮(zhèn)靜鋼
S355J2W 化學(xué)元素成分含量(%)
成分
C
Si
Mn
P
S
Cr
Ni ③
Cu
Mo ③
Zr ③
長(zhǎng)形產(chǎn)品
最小值
-
-
0.5
-
-
0.4
-
0.25
-
-
最大值
0.16
0.5
1.5
0.03
0.03
0.8
0.65
0.55
0.3
0.15
成分
C
Si
Mn
P
S
Cr
Ni ③
Cu
Mo ③
Zr ③
最小值
-
-
0.5
-
-
0.4
-
0.25
-
-
最大值
0.16
0.5
1.5
0.035
0.035
0.8
0.65
0.55
0.3
0.15
①FN=rimming steels not permitted(不允許沸騰鋼);FF=fully killed steel(完全鎮(zhèn)靜鋼)
②The steels contain at least one of the following elements: Al total≥0.02%,Nb:0.015~0.06%,V:0.02~0.12%,Ti:0.02~0.1%。If these elements are used in combination, at least one them shall be present with the minimum content indicated。(鋼應(yīng)至少含有下列元素之一:Al總含量為≥0.020%,Nb:0.015 ~ 0.060%,V:0.02 ~ 0.12%,Ti:0.02 ~ 0.10%。如果將這些元素組合使用,其中至少有一種元素應(yīng)具有所示的最低含量。)
③鋼中Ni、Mo、Zr含量可達(dá)的最大值
④當(dāng)Si的最低含量為0.15%時(shí),Cr含量可降至0.37%
S355J2W 機(jī)械性能
厚度
t
mm
抗拉強(qiáng)度 σb
Mpa
屈服點(diǎn) σs
Mpa
斷后伸長(zhǎng)率或延伸率 δ
%
t<3
510~680
≥355
見(jiàn)備注
3≤t≤16
470~630
≥355
≥22
16<t≤40
470~630
≥345
≥22
40<t≤63
470~630
≥335
≥21
63<t≤80
470~630
≥325
≥20
80<t≤100
470~630
≥315
≥20
100<t≤150
450~600
≥295
≥18
①公稱厚度1.5<t≤2時(shí),斷后延伸率δ≥16
②公稱厚度2<t≤2.5時(shí),斷后延伸率δ≥17
③公稱厚度2.5<t<3時(shí),斷后延伸率δ≥18
近似對(duì)照表 結(jié)構(gòu)、壓力容器和工程鋼
日本
美國(guó)
德國(guó)
歐標(biāo)
JIS
ASTM
DIN EN/DIN
EN
數(shù)字牌號(hào)
SMA50CP
A709-50W
WTSt52-3
S355J2W
S355J2G2W①
1.8965